Title: Investigation of mechanical properties resintered UO2 pellets by micro hardness method
Other Titles: Yeniden sinterlenen UO2 pelletlerinin mekanik özelliklerinin mikro sertlik metoduyla incelenmesi
Authors: Akbal, Sevgi
Yaylı, Ahmet
Can, Ferhan
Keşaf, Esra
TAEK-Teknoloji Geliştirme Dairesi
Keywords: Re-sintering
Yeniden sinterleme
Thermal stability test
Termal kararlılık testi
Micro hardness
Mikrosertlik
Mechanical properties
Mekanik özellikler
Microstructure
Mikroyapı
UO2
Issue Date: Jun-2019
Publisher: Turkish Atomic Energy Authority
Citation: Akbal, S. ... [ve arkadaşları]. (2019). Investigation of mechanical properties resintered UO2 pellets by micro hardness method. Turkish Journal of Nuclear Sciences, 31(1), 24-29.
Abstract: Bu çalışmanın amacı, mikro sertlik testi kullanılarak re-sinter UO2 yakıt peletlerinin mekanik özelliklerinin incelenmesidir. UO2 yakıt peletleri toz metalurjisi yolu ile üretilmiştir. Ar +% 5 H2 atmosferinde 4 saat sinterleme ile üretilen UO2 peletleri, termal kararlılık testi için Ar +% 5 H2 atmosferinde 24 saat boyunca 1700 0C'de yeniden sinterlemeye tabi tutulmuştur. Termal kararlılık testinin UO2 peletlerinin mekanik ve mikroyapı özelliklerine etkisi tartışılmıştır.
Thermal stability test (re-sintering test) of the nuclear fuel is one of the most important characterization steps before loading to the reactor. The purpose of this study is investigation of mechanical properties of re-sintered UO2 pellets using micro hardness test method. UO2 fuel pellets were produced by powder metallurgical route. UO2 pellets sintered for 4 hours at Ar + 5% H2 atmosphere were subjected to re-sintering at 1700 0 C for 24 hours in Ar + 5% H2 atmosphere for thermal stability test. Re-sintering effects on the mechanical properties and microstructure of UO2 pellets were investigated.
URI: https://dergipark.org.tr/tr/pub/tjns/issue/46345/463154
http://kurumsalarsiv.tenmak.gov.tr/handle/20.500.12878/1601
ISSN: 0254-5446
Appears in Collections:Volume 31 Sayı 1

Files in This Item:
File Description SizeFormat 
tjns_60015.pdf828.67 kBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.